Influence of substrate, cement and aging on the biaxial flexural strength of lithium disilicate / Influência do substrato, cimento e envelhecimento na resistência a flexão biaxial do dissilicato de lítio

Objective: To evaluate the biaxial flexural strength (BFS) of lithium disilicate (L), cemented on different substrates (epoxy resin - E and metal - M) with dual-cure resin cement (Rc) and zinc phosphate cement (Zc), not aged, thermally aged (TC) or thermo-mechanical aged (TC/MC). Material and Methods: Disks of L, E, and M were fabricated, and the cementation was performed according to the following groups: ERc (L+E+Rc); MRc (L+M+Rc); MZc (L+M+Zc); EZc (L+E+Zc). Ten samples from each described group were tested in BFS, ten more samples were subjected to TC (1×104 cycles between 5 ºC and 55 ºC water), and the last 10 samples were subjected to TC/MC (MC: 1.2×106 cycles, 50 N, 3.8 Hz). The BFS test was performed and scanning electron microscopy (SEM) was performed to evaluate the failure mode. The effect of the cementation strategy (cement/substrate) was compared in each aging method and the effect of the aging method was evaluated for each cementation strategy by one-way ANOVA and Tukey post-hoc test (α=0.05). Results: The strength values were highest to M (237.8 ~ 463.9 MPa), in comparison to the E (41.03 ~ 66.76 MPa), despite aging and luting agent. Flexural strength data decreased after TC and TC/MC in groups cemented with Zc, but was stable when cemented with Rc. SEM analysis indicated that failure origins were located at the tensile surface of the L. Conclusion: Lithium disilicate discs cemented to the metallic substrate presented the highest biaxial flexural strength. The cementation with dual-cure resin cement did not decrease BFS after aging (AU)

Objetivo: Avaliar a resistência à flexão biaxial (BFS) do dissilicato de lítio (L), cimentado sobre diferentes substratos (resina epóxi - E e metal - M) com cimento resinoso dual (Rc) e cimento de fosfato de zinco (Zc), não envelhecido, submetido ao envelhecido térmico (TC) ou ao envelhecido térmico-mecânico (TC/MC). Material e Métodos: Foram confeccionados discos de L, E e M, e a cimentação foi realizada de acordo com os seguintes grupos: ERc (L+E+Rc); MRc (L+M+Rc); MZc (L+M+Zc); EZc (L+E+Zc). Dez amostras de cada grupo descrito foram testadas em BFS, mais dez amostras foram submetidas à TC (1×104 ciclos de imersão em água entre 5 ºC e 55 ºC), e as últimas 10 amostras foram submetidas à TC/MC (MC: 1.2 ×106 ciclos, 50 N, 3.8 Hz). Foram realizados os testes de BFS e a microscopia eletrônica de varredura (MEV) para avaliar o modo de falha. O efeito da estratégia de cimentação (cimento/substrato) foi comparado em cada método de envelhecimento e o efeito do método de envelhecimento foi avaliado para cada estratégia de cimentação por ANOVA a um fator e teste post-hoc de Tukey (α=0,05). Resultados: Os valores de resistência foram maiores para M (237.8 ~ 463.9 MPa), em comparação com E (41.03 ~ 66.76 MPa), independentemente do envelhecimento e do agente cimentante utilizado. Os dados de resistência à flexão diminuíram após TC e TC/MC nos grupos cimentados com Zc, mas se mantiveram estáveis quando cimentados com Rc. A análise MEV indicou que a origem das falhas estava localizada na superfície de tração do L. Conclusão: Os discos de dissilicato de lítio cimentados ao substrato metálico apresentaram maior resistência à flexão biaxial. A cimentação com cimento resinoso dual não diminuiu o BFS após o envelhecimento (AU)

Effect of repeated firings and staining on the mechanical behavior and composition of lithium disilicate.

OBJECTIVE: To evaluate the composition, flexural strength and fatigue behaviour of lithium disilicate ceramic (LD) after repeated firings and different staining techniques. METHODS: LD discs were fabricated and divided according to number of firing cycles and staining technique: CO - control, discs were crystallized (850°C/10min); SC - single-step characterization - crystallization and staining (applied with a thin brush) were performed in a single step with one firing cycle (850°C/10min); and DC - double-step characterization - crystallization firing cycle was performed first (850°C/10min), followed by staining firing cycle (770°C/90s). Specimens were fired two, four or six times (one crystallization firing cycle and one, three or five staining firing cycles), resulting into 9 groups (n=30): COII, COIV, COVI, SCII, SCIV, SCVI, DCII, DCIV and DCVI. The composition of the specimens was investigated (EDS, XRD, Raman spectroscopy), and the biaxial flexural strength (n=10) and staircase tests (n=20, 5×104 cycles, 5Hz) were performed. Data were subjected to one-way ANOVA and Tukey's test (α=0.05). RESULTS: EDS and XRD revealed amorphous content for stained groups. Biaxial flexural strength was not affected by repeated firings in any group, but stained groups presented lower flexural strength than control groups (p=0.001). The fatigue limit results decreased in all groups compared to flexural strength. SC groups showed similar (SCII and SCIV) or even higher fatigue limits (SCVI) than the control groups, and DC showed the lowest fatigue limit values. SEM and Raman suggested that the interfaces between staining and the LD showed only an overlap for the DC groups, whereas for the SC it was suggested an interaction between the stain and the LD. SIGNIFICANCE: Repeated firings did not result in decreased lithium disilicate flexural strength.Staining affected flexural strength and also resulted in increased amorphous content in the characterized specimens. Single-step staining resulted in the highest fatigue limit.

Can the silane heat treatment influence the bond durability between resin cements and a dental ceramic? / O tratamento térmico do silano pode influenciar na durabilidade da adesão entre cimento e cerâmica dental?

ABSTRACT Objective Evaluate the influence of silane heat treatment in bond durability between two resin cements and CAD/CAM feldspathic ceramic. Methods 40 feldspathic ceramic blocks were obtained, and were duplicated in microhybrid composite. All ceramic blocks were etched with 10% hydrofluoric acid for 20 s and received application of silane agent. The blocks were randomizedinto eight groups (n=5) according to the surface treatments and luting agents: P- Panavia F; PAg- Panavia F + Aging; HP- Heat Treatment + Panavia F; HPAg- Heat Treatment + Panavia F + Aging; R- RelyX ARC; Rag- RelyX ARC + Aging; HR- Heat Treatment + RelyX ARC; HRAg- Heat Treatment + RelyX ARC + Aging. The heat treatment was performed in furnace at 100 °C for 2 min. All blocks were cemented and cut to obtain samples with adhesive area of 1 mm2. Aging was performed with 10000 thermal cycles. The samples were subjected to microtensile bond strength test. Results The three-way ANOVA test revealed a significant interaction between cement versus heat treatment (p=0.001) and heat treatment versus thermal cycling (p=0.001) indicating that there was a change in bond strength due to surface treatment and aging. Conclusion Therefore, the heat treatment of the silane at 100 ºC for 2 minutes obtained higher values of bond strength between the resin cement and a feldspathic ceramicafter aging.

RESUMO Objetivo Avaliar a influência do tratamento térmico do silano na resistência de união entre dois cimentos resinosos e uma cerâmica feldspática CAD/CAM. Métodos Quarenta blocos cerâmicos foram duplicados em resina micro-híbrida. Todas as cerâmicas foram condicionadas com ácido fluorídrico 10% por 20 s e receberam aplicação do silano. Os blocos foram randomizados em oito grupos (n = 5): P-Panavia F; PAg- Panavia F + Envelhecimento; HP-Tratamento térmico + Panavia F;HPAg-Tratamento térmico + Panavia F + Envelhecimento; R-RelyX ARC; RAg-RelyX ARC; HR-Tratamento térmico + RelyX ARC; HRAg - Tratamento térmico + RelyX ARC + Envelhecimento. O tratamento térmico foi realizado em forno a 100 °C durante2 min. Todos os blocos foram cimentados e cortados para obter amostras para microtração. Foram feitos 10000 ciclos térmicos. As amostras foram submetidas a teste de micro-tração. Resultados O teste ANOVA revelou uma interação significativa entre cimento/tratamento térmico (p=0,001) e tratamento térmico/ciclo térmico (p=0,001). Conclusão Dessa maneira, o tratamentotérmico do silano a 100ºC por 2 minutos foi capaz de aumentar a resistência de união entre o cimento resinoso e uma cerâmica feldspática mesmo após o envelhecimento.

Can the size and the luting material influence in the bond strength of the fiberglass post to dentin? / O comprimento e o tipo de cimento podem influenciar na adesão do pino de fibra de vidro a dentina?

Aim: To evaluate the influence of lengths and different luting agents on the bond strength of fiberglass posts' adhesion to dentin.Methods: Sixty single-root bovine teeth were endodontically treated and included in polyether and acrilyc resin to simulate a periodontal ligament. These were divided into 6 groups according to the post lengths (6, 10 or 14 mm) and luting agents (self-adhesive dual resin cement ­ U; or etch-and-rinse dual resin cement ­ A): U6, U10, U14, A6, A19, and A14. All fiberglass posts were cemented according to manufacturer instructions. After this, mechanical aging was performed (1.2x106 cycles; 4 Hz, 90 N). The push-out specimens were then conducted (2.0 ± 0.1 mm), with the test executed in a universal machine (10 kgf at 0.5 mm/min). Data obtained were submitted to the Kruskal-Wallis and Dunn's test. Results: No statistically significant difference was observed in bond strength between the groups due to the type of luting agent (p > 0.05). However, the isolated post-length factor showed significantly different results for the U groups (p < 0.05). The U10 group showed similar union values to U6 but statistically inferior to U14. Conclusion: bond strength of fiberglass posts of the same length as the dentin presented no differences according to the luting agent, but the post-length property influenced the bond strength when self-adhesive resin cement was used.

Objetivo: avaliar a influência dos agentes cimentantes e dos diferentes comprimentos de pinos na resistência de união de pinos de fibra de vidro a dentina. Métodos: Sessenta dentes bovinos uniradiculares tiveram a raiz endodonticamente tratada, e foram incluídos em poliéter e resina acrílica para simular o ligamento periodontal. Os espécimes foram divididos em seis grupos de acordo com o comprimento dos pinos (6, 10 ou 14mm) e dos agentes de cimentantes (cimento resinoso dual autoadesivo (RelyX U200, 3M ESPE) - U; ou cimento resinoso dual convencional (AllCem Core, FGM) - A: U6, U10, U14, A6, A19 e A14. Todos os pinos de fibra de vidro foram cimentados conforme as recomendações do fabricante. Após, o envelhecimento mecânico (1,2x106 ciclos; 4 Hz, 90 N) as amostras foram fatiadas para o teste de push-out (2,0 ± 0,1 mm) executado em uma máquina de ensaio universal (10 kgf a 0,5 mm/min). Os dados foram submetidos ao teste de Kruskal-Wallis e Dunn. Resultados: não houve diferença estatística na resistência de união entre os grupos devido ao tipo de agente cimentante (p > 0,05), mas houve para o comprimento dos pinos dos grupos U (p < 0,05). O grupo U10 apresentou valores de união semelhantes a U6, mas estatisticamente inferiores ao U14. Conclusão: a resistência de união dos pinos de fibra de vidro de um mesmo comprimento não apresentou diferenças mesmo quando cimentados com cimentos diferentes, mas o comprimento dos pinos isoladamente influenciou quando o cimento resinoso autoadesivo foi utilizado.

Influence of surface treatments in flexural strength and superficial topography of a lithium disilicate ceramic / Influência dos tratamentos de superfície na resistência à flexão e na topografia superficial de uma cerâmica de dissilicato de lítio

Objective: The aim of the study was to evaluate the influence of different surface post-etching treatments in flexural strength, contact angle and surface roughness of a lithium disilicate ceramic. Material and Methods: 60 bars (16 x 2 x 4 mm) were divided in six groups (n=10): C, no treatment; HF, hydrofluoric acid for 20 s (HF) + washing (60 s), drying (30s); HFL, HF + washing (60 s), drying (30 s) and luting; HFNL, HF + washing (60 s) + neutralization with sodium bicarbonate (SB) for 40 s + washing (5s), drying (30 s) and luting; HFUL, HF + washing (60 s) + ultrasonic bath (UB) for 4 min, drying (30 s) and luting; HFNUL, HF + washing (60 s) + SB (40 s) + UB (4 min) and luting. The bars were submitted to three-points flexural strength test. 25 ceramic blocks (12 x 7 x 7 mm) were divided into five groups (n=5) to evaluate roughness and contact angle C - no treatment; HF - HF ; HFU - HF and UB for 5 min ; HFN - HF and SB; HFNU - HF, UB and SB. A scanning electron microscope (SEM) showed the surface of the samples. ANOVA one-way statistical analysis was done for comparison of results. Results: There was no statistical difference for flexural strength (p-value = 0.15) and for surface roughness (p-valor = 0.15). However, it was obtained statistically significant difference for contact angle (p-valor = 0.00). SEM images showed precipitates after the acid etching, which were removed by post-etching treatments. Conclusion: It can be concluded that the different post-etching surface treatments did not increase the flexural strength, surface roughness, but it influenced the ceramic wetting and SEM images (AU)

Objetivo: O objetivo do estudo foi avaliar a influência de diferentes tratamentos pós-condicionamento na resistência à flexão, ângulo de contato e rugosidade superficial de uma cerâmica de dissilicato de lítio. Material e Métodos: 60 barras (16 x 2 x 4 mm) foram divididas em seis grupos (n = 10): C, sem tratamento; HF, ácido fluorídrico durante 20 s (HF) + lavagem (60 s), secagem (30 s); HFL, lavagem com HF + (60 s), secagem (30 s) e cimentação; HFNL, HF + lavagem (60 s) + neutralização com bicarbonato de sódio (SB) por 40 s + lavagem (5s), secagem (30 s) e cimentação; HFUL, HF + lavagem (60 s) + banho ultrassônico (UB) por 4 min, secagem (30 s) e cimentação; HFNUL, HF + lavagem (60 s) + SB (40 s) + UB (4 min) e cimentação. As barras foram submetidas ao teste de resistência à flexão de três pontos. 25 blocos cerâmicos (12 x 7 x 7 mm) foram divididos em cinco grupos (n = 5) para avaliação da rugosidade superficial e ângulo de contato C - sem tratamento; HF - HF; HFU - HF e UB por 5 min; HFN - HF e SB; HFNU - HF, UB e SB. Um microscópio eletrônico de varredura (MEV) foi utilizado para análise da superfície das amostras. A análise estatística unidirecional ANOVA-um fator foi realizada para comparação dos resultados. Resultados: Não houve diferença estatística para a resistência à flexão (p-valor = 0,15) e para a rugosidade superficial (p-valor = 0,15). No entanto, obteve-se diferença estatisticamente significante para o ângulo de contato (p-valor = 0,00). Imagens de microscopia eletrônica de varredura mostraram a formação de precipitados após o ataque ácido, que foram removidos pelos tratamentos pós-condicionamento. Conclusão: Pode-se concluir que os diferentes tratamentos de superfície pós-condicionamento não aumentaram a resistência à flexão, rugosidade da superfície, mas influenciaram na molhabilidade da cerâmica e nas imagens em MEV.(AU)

Color assessment in dental prostheses: the use of smartphones as process tools / Tomada de cor em prótese dentária: Uso de celular como auxílio do processo

Accurate color selection of direct or indirect dental restorations is a subjective task. Mobile phones are tools that may minimize color assessment errors. The objective was to use photographs taken with smartphones to guide the dental surgeon in choosing the right color in oral rehabilitation. A tooth was photographed for color assessment and the VITA Toothguide 3D-MASTER® shade guide was used. Photographs were submitted to an image editing software for full saturation removal. Images of the tooth and scale in black and white were compared. This method allowed to select the tooth's value, which is considered the most subjective dimension in color choice. Although it is an auxiliary and complementary method to traditional methods, smartphones are tools capable of reducing the range of color possibilities and minimizing possible failures (AU)

A correta seleção da cor das restaurações dentais diretas ou indiretas é uma atividade subjetiva. Os celulares são ferramentas que podem minimizar os erros da tomada de cor. O objetivo foi utilizar fotografias realizadas com smartphones para orientar o cirurgião-dentista na escolha da cor em reabilitação oral. Foi fotografado um dente para tomada de cor e a escala Vita 3D Master. As imagens foram submetidas a um software de edição de imagem para remoção total da saturação. As imagens em preto e branco do dente e da escala foram comparadas. A metodologia permitiu selecionar o valor do dente que é o aspecto considerado mais subjetivo na escolha da cor. Apesar de ser um método auxiliar e complementar aos métodos tradicionais é uma ferramenta capaz de diminuir o leque de possibilidades de cores e minimizar possíveis falhas (AU)

Different surface treatment protocols of a Y-TZP ceramic with a superficial glaze layer

Aim: evaluate the influence of etching time with hydrofluoric acid on the bond strength of a Yttrium-stabilized polycrystalline tetragonal zirconia (Y-TZP) ceramic with a superficial glaze layer and a resin cement. Methods: Y-TZP blocks were cut to obtain 40 samples. They were distributed into four groups (n = 10): control treated by sandblasting with silica-coated alumina (RS) and three glazed experimental groups with different etching times: GS20s, GS60s and GS100s. Cementation was done with a universal adhesive and a resin cement. Two cement cylinders were made in each block. After thermocycling, the shear bond test was performed. Two extra samples of each group were made to obtain profilometry, scanning electron microscopy, mapping and backscattered electron detector images. Energy dispersive spectrometry and goniometry were also performed. Results: Kruskal-Wallis and Dunn tests demonstrated bond strength differences only between the RS (22.10MPa) and the GS groups (GS20s: 8,10Mpa; GS60s: 10.49MPa; GS100s: 7.53MPa) (p = 0.001), but there was no difference among the experimental groups (p > 0.05). The contact angles were 55.33º (RS); 70.78° (GS100s); 48.20º (GS60s) and 28.73º (GS20s). ANOVA and Tukey test demonstrated similar wettability of RS to GS60s and GS100s (p > 0.05), but all the experimental groups were statistically different between them (p < 0.001). Qualitative image analysis revealed an irregular glaze distribution after etching. The thickness of the remaining glaze layer measured by profilometry was 5±1µm (GS20S), 4±1µm (GS60S) and 3±1µm (GS100s). Conclusion: The etching time of glazed zirconia did not influence the adhesive strength of the ceramic to the resin cement

Bond and topography evaluation of a Y-TZP ceramic with a superficial low-fusing porcelain glass layer after different hydrofluoric acid etching protocols / Avaliação da adesão e topografia de uma zircônia Y-TZP com uma camada de glaze após diferentes protocolos de condicionamento com ácido fluorídrico

Introduction: Despite being one of the most studied ceramics today, zirconia still does not have a well-defined adhesion protocol. Objective: Evaluate the influence of different etching times and hydrofluoric acid (HF) concentrations on the zirconia surface and bond strength between a vitrified Y-TZP ceramic and a resin cement. Materials and method: The zirconia surface treatments were: sandblasting with silica-coated alumina (Co); glaze application + 5% HF etching for 5s (G5-5s), 10s (G5-10s) or 20s (G5-20s); glaze application + 10% HF etching for 5s (G10-5s), 10 (G10-10s) or 20s (G10-20s) . Then, cement cylinders (3.3 × 3.3 mm) were built up for shear bond test on all specimens. The specimens were subjected to 6000 thermal cycling before the test. Fractures were analyzed by stereomicroscope. Data were statistically analyzed by Kruskal-Wallis and Dunn statistical tests (5%). Extra samples of each group were made to obtain profilometry and scanning electron microscopy (SEM). Result: Zirconia-cement bond strength was affected by the ceramic surface treatments (p = 0.001). G10-5s (2.71 MPa) recorded the highest bond strength values, followed by the Co (2.05 MPa) while G5 groups had the lowest bond value. Adhesive failure of the samples predominated. The image analysis revealed G5 groups seem to have a lower roughness when compared to groups treated by 10% HF. The creation of pores in the low-fusing porcelain glass layer surface occurred only when 10% HF was used. Conclusion: The low-fusing porcelain glass layer application was able to overcome the sandblasting and obtain a greater adhesive bond to the resinous cement, however, only when 10% HF was used for an interval of 5 seconds.

Introdução: Apesar de ser uma das cerâmicas mais estudadas atualmente, a zircônia ainda não possui um protocolo bem definido para uma cimentação adesiva. Objetivo: Avaliar a influência de diferentes tempos de condicionamento e concentrações do ácido fluorídrico (AF) na superfície da zirconia e na resistência de união entre uma cerâmica Y-TZP vitrificada e um cimento resinoso. Material e método: Os tratamentos de superfície foram: jateamento com óxido de alumínio revestido com sílica (Co); aplicação de glaze + condicionamento com AF 5% por 5s (G5-5s), 10s (G5-10s) ou 20s (G5-20s); aplicação de glaze + condicionamento com AF 10% por 5s (G10-5s), 10 (G10-10s) ou 20s (G10-20s). Em seguida, cilindros de cimento (3,3 × 3,3mm) para teste de cisalhamento foram feitos em todos os espécimes. Os espécimes foram submetidos a 6000 ciclos térmicos antes do teste de adesão. As fraturas foram analisadas por estereomicroscópio. Os dados foram analisados ​​estatisticamente por Kruskal-Wallis e Dunn (5%). Amostras extra de cada grupo foram feitas para realização de perfilometria e microscopia eletrônica de varredura (MEV). Resultado: A resistência de união zircônia-cimento foi afetada pelos tratamentos de superfície (p = 0,001). Os grupos G10-5s (2,71 MPa) registraram os maiores valores de resistência de união, seguidos pelos Co (2,05 MPa), enquanto os grupos G5 apresentaram o menor valor de união. Falhas adesivas foram predominantes. As análises por imagem revelaram que os grupos G5 parecem ser menos rugosos quando comparados aos grupos tratados com AF 10%. A criação de poros na superfície vítrea (glaze) ocorreu apenas quando foi utilizado AF 10%. Conclusão: A aplicação de camada de vidro de porcelana de baixa fusão foi capaz de superar o jateamento e obter uma maior adesão adesiva ao cimento resinoso, no entanto, somente quando foi utilizado 10% de HF por um intervalo de 5 segundos.

Can low-fusing glass application affect the marginal misfit and bond strength of Y-TZP crowns?

To evaluate the effect of different surface treatments on the marginal misfit and retentive strength between Y-TZP crowns and an epoxy resin. Forty (40) epoxy resin (G10) abutments (height: 5mm, conicity: 60, finish line: large chamfer) with equal dimensions were milled and included in polyurethane to simulate the periodontal ligament. Next, 40 Y-TZP crowns (thickness: 1mm) were milled (Cerec in Lab) and randomly divided into four groups (n=10) according to the surface treatment: GS(glaze spray), GP(glaze powder/liquid), P(zirconia primer) and RS(tribochemical silica coating). The conditioned surfaces were cemented with dual self-adhesive cement, light cured and submitted to thermomechanical cycling (2x106, 100N, 4Hz, 5°/55°C). Marginal misfit was analyzed by a stereomicroscope and SEM. Retentive strength test was performed (1mm/min) until crown debonding. Glaze layer thickness was also performed to GS and GP groups. Marginal misfit data were analyzed by Kruskal Wallis and Dunn tests; one-way ANOVA and Tukey (5%) analyzed the tensile strength data. The marginal misfit of the GS (48.6±19.9µm) and GP (65.4±42.5µm) were statistically lower than the RS (96±62.9µm) and P (156±113.3µm) (p=0.001). The retentive strength of the GP (470.5±104.1N) and GS (416.8±170.2N) were similar to the P (342.1±109.7N), but statistically higher than those of the RS (208.9±110N). The GS and GP glaze layer was 11.64µm and 9.73µm respectively. Thus, glaze application promoted lower marginal discrepancy and higher retentive strength values than conventional techniques.

Effect of fatigue protocols on flexural strength of lithium disilicate bars with clamped-ends.

The aim of this study was compare the effect of two in vitro ageing protocols to intraoral aging on the flexural strength of a lithium disilicate (LD) ceramic bars with clamped ends. After polishing and crystallization, the both ends of the bars were cemented to a metallic device and subjected to mechanical cycling, thermomechanical cycling, or intraoral ageing. Ten volunteers used an intraoral device - similar to an occlusal splint with a balanced contact condition on the occlusal surface of the ceramic bar - during 8 h night time / 30 days. Both in vitro and intraoral ageing decreased the flexural residual strength of LD, with the lowest values obtained after intraoral ageing. Thus, the in vitro ageing protocols tested in this study revealed to be less deleterious than intraoral ageing of LD.

Can low-fusing glass application affect the marginal misfit and bond strength of Y-TZP crowns?

Abstract To evaluate the effect of different surface treatments on the marginal misfit and retentive strength between Y-TZP crowns and an epoxy resin. Forty (40) epoxy resin (G10) abutments (height: 5mm, conicity: 60, finish line: large chamfer) with equal dimensions were milled and included in polyurethane to simulate the periodontal ligament. Next, 40 Y-TZP crowns (thickness: 1mm) were milled (Cerec in Lab) and randomly divided into four groups (n=10) according to the surface treatment: GS(glaze spray), GP(glaze powder/liquid), P(zirconia primer) and RS(tribochemical silica coating). The conditioned surfaces were cemented with dual self-adhesive cement, light cured and submitted to thermomechanical cycling (2x106, 100N, 4Hz, 5°/55°C). Marginal misfit was analyzed by a stereomicroscope and SEM. Retentive strength test was performed (1mm/min) until crown debonding. Glaze layer thickness was also performed to GS and GP groups. Marginal misfit data were analyzed by Kruskal Wallis and Dunn tests; one-way ANOVA and Tukey (5%) analyzed the tensile strength data. The marginal misfit of the GS (48.6±19.9μm) and GP (65.4±42.5μm) were statistically lower than the RS (96±62.9μm) and P (156±113.3μm) (p=0.001). The retentive strength of the GP (470.5±104.1N) and GS (416.8±170.2N) were similar to the P (342.1±109.7N), but statistically higher than those of the RS (208.9±110N). The GS and GP glaze layer was 11.64μm and 9.73μm respectively. Thus, glaze application promoted lower marginal discrepancy and higher retentive strength values than conventional techniques.

The influence of disinfection on dimensional stability of temporary crowns / A influência da desinfecção na estabilidade dimensional de coroas temporárias

Objective: Evaluate the influence of different disinfection methods on the dimensional stability of temporary acrylic resin crowns. Material and Methods: A metallic die with two different marks at the margin was used to prepare the specimens with two different resins (bis-acrylic resin-Structur, acrylic resin-Dencrilay). They were divided into eight groups (n=8), determined according to the disinfection methods (microwave, acetic acid, 1% hypochlorite) and control. The marginal adaptation was recorded using an optical microscope (50X) comparing two different marks on the margin of the crowns with 2 points along the entire circumferential margin before and after disinfection methods. Results: Results were compared statistically by ANOVA and Tukey's test (p≤0.05). The two-way ANOVA showed statistical difference between types of materials. No significant differences were found between disinfection methods and interaction of factors. Conclusion: All procedures affected the marginal adaptation however temporary crowns made by bis-acrylic resin demonstrate higher dimensional stability. (AU)

Objetivo: Avaliar a influência de diferentes métodos de desinfecção na estabilidade dimensional de coroas temporárias de resina acrílica. Material e Métodos: um molde metálico com duas marcas diferentes na margem foi utilizado para preparar os espécimes com duas resinas diferentes (resina bis-acrílica - estrutura, resina acrílica-Dencrilay). Eles foram divididos em oito grupos (n = 8), determinados de acordo com os métodos de desinfecção (microondas, ácido acético, 1% de hipoclorito) e controle. A adaptação marginal foi registrada usando um microscópio óptico (50X) comparando duas marcas diferentes na margem das coroas com 2 pontos ao longo de toda a margem circunferencial antes e após os métodos de desinfecção. Resultados: os resultados foram comparados estatisticamente por ANOVA e teste de Tukey (p≤0,05). A ANOVA de dois fatores mostrou diferença estatística entre os materiais utilizados. Não foram encontradas diferenças significativas entre os métodos de desinfecção e a interação dos fatores. Conclusão: Todos os procedimentos afetaram a adaptação marginal, porém as coroas temporárias feitas em resina bis-acrílica demonstram maior estabilidade dimensional. (AU)

Effect of thermocycling aging on the flexural strength of feldspathic ceramic / Efeito da termociclagem na resistência flexural de uma cerâmica feldspática

Objective: The aim of the study was to evaluate the effect of aging through different thermocycling protocols on the flexural strength of a feldspathic ceramic. Material and Methods: Fifty ceramic bars, Vitablock Mark II (VITA), with dimensions of 18X4X2mm were prepared. The bars were randomly distributed to the groups (n = 10), which were defined according to the number of thermal cycles (TCy): G0 - no TCy; G500 - 500 cycles of TCy; G6000 - 6000 TCy; G10000 - 10000 TCy; G15000 - 15000 TCy. After aging, the specimens were subjected to the three point bending test in a universal testing machine (EMIC DL 1000), under 0.5mm/min speed and loading of 50kgf, until catastrophic failure. A sample of each group was evaluated for topographic morphology under Scanning Electron Microscopy. Results: For mechanical testing, the following mean values and standard deviation (MPa) were obtained: G0 (99.78 ± 5.07); G500 (101.64 ± 5.59); G6000 (98.13 ± 4.95); G10000 (91.77 ± 9.68); G15000 (101.51 ± 4.22). An analysis of variance by regression equation (p = 0.387) was performed, demonstrating a weak and non-significant correlation between flexural strength and number of thermal cycles. Conclusion: It can be concluded that aging in water solely by different numbers of temperature cycles did not influence on the flexural strength of a feldspathic ceramic. (AU)

Objetivo: O objetivo do estudo foi avaliar o efeito do envelhecimento por meio de diferentes protocolos de ciclos térmicos na resistência à flexão de uma cerâmica feldspática. Material e Métodos: Cinquenta barras de cerâmica, Vitablock Mark II (VITA), com dimensões de 18X4X2mm foram preparadas. As barras foram distribuídas aleatoriamente pelos grupos (n = 10), os quais foram definidos de acordo com o número de ciclos térmicos (CT): G0 ­ nenhum; G500 - 500 CT; G6000 - 6000 CT; G10000 ­ 10000 CT; G15000 - 15000 CT. Após envelhecimento, as amostras foram submetidas ao ensaio de flexão de três pontos em uma máquina de ensaios universal (EMIC DL 1000), sob a velocidade de 0,5 mm / min e célula de carga de 50kgf, até uma falha catastrófica. Uma amostra de cada grupo foi avaliada quanto à morfologia topográfica sob microscopia eletrônica de varredura. Resultados: Para os testes mecânicos, foram obtidos os seguintes valores médios e desvio padrão (MPa): G0 (99,78 ± 5,07); G500 (101,64 ± 5,59); G6000 (98,13 ± 4,95); G10000 (91,77 ± 9,68); G15000 (101,51 ± 4,22). Uma análise de variância pela equação de regressão (p = 0,387) foi realizada, o que demonstra uma correlação fraca e não significativa entre a resistência à flexão e do número de ciclos térmicos. Conclusão: Pode-se concluir que o envelhecimento somente em água por diferentes números de ciclos térmicos não influenciou na resistência à flexão de uma cerâmica feldspática (AU)

Influence of indirect reinforcements on the flexural strength of a thermally activated acrylic resin used for complete dentures / Influência de reforços indiretos na resistência a flexão de uma resina acrílica ativada térmicamente utilizada na confecção de próteses totais

Objective: This research aimed to verify the performance of thermally activated acrylic resin (TAAR) combined with a mix of glass and aramid fibers and/or composite resin of indirect use by a tree point bending test. Material and Methods: Ten samples, with 65 x 10 x 2.5 mm, were prepared for each group (n = 10): CO, control of only TAAR; CR, in which an 60 mm indirect composite resin was polymerized together with the acrylic resin during the thermo-polymerization cycle; SS, in which ceramic glass mixed with aramid fibers cut 60 mm in length were incorporated into the samples; and SC, in which the same fibers were incorporated with addiction of the indirect composite resin. A three point flexural strength test was performed with a universal testing machine with a load of 50KgF at a speed of 5 mm/min in the center of the samples supported by a suitable device. The reinforced face was placed to the tensile side. The statistical one way ANOVA and Tukey tests were made with a significance level of 95%. Results: The mean value for the CO was 60,27 ± 24,18 MPa, for CR it was 38,39±12,75 MPa, for SS it was 79,97±12,75 Mpa and for CS it was 32,40±9,05 MPa. Conclusion: The use of glass and aramid fibers at the base of a TAAR increased the three-point flexural strength, however when indirect composite resin was incorporated, a significant drop of this mechanical property was observed. (AU)

Objetivo: Esta pesquisa teve como objetivo verificar o desempenho de uma resina acrílica ativada termicamente (RAAT) combinada com uma mistura de fibras de vidro e aramida e / ou resina composta de uso indireto por um teste de flexão de três pontos. Material e Métodos: Foram preparadas dez amostras, com 65 x 10 x 2,5 mm, para cada grupo (n = 10): CO, controle com apenas RAAT; CR, em que uma resina composta indireta de 60 mm com polimerizada em conjunto com a resina acrílica durante o ciclo de termopolimerização; SS, em que o vidro cerâmico misturado com fibras de aramida cortadas com 60 mm de comprimento foi incorporado nas amostras; e SC, nas quais as mesmas fibras foram incorporadas em conjunto com a resina composta indireta. O teste de resistência à flexão de três pontos foi realizado em uma máquina de teste universal com uma carga de 50 KgF a uma velocidade de 5 mm/min no centro das amostras suportadas por um dispositivo adequado. A face reforçado foi colocado no lado da tração. Os testes estatísticos one-way ANOVA e Tukey foram feitos com um nível de significância de 95%. Resultados: O valor para o CO foi de 60,27 ± 24,18 MPa, para CR foi de 38,39 ± 12,75 MPa, para SS foi de 79,97 ± 12,75 Mpa e para CS foi de 32, 40 ± 9,05 MPa. Conclusão: o uso de fibras de vidro e aramida na base de uma RAAT aumentou a resistência à flexão de três pontos, no entanto, quando a resina composta indireta foi incorporada, observou-se uma queda significativa dessa propriedade mecânica (AU)

Avaliação dos hábitos de higiene bucal em portadores de prótese total associados à prevalência de lesões bucais / Evaluation of oral hygiene in complete dentures users associated with the prevalence oral lesions

[{"text": "desdentados, apesar de ser considerada facilitadora de várias patologias bucais. Assim, o objetivo deste estudo foi conhecer os hábitos de higiene bucal dos usuários de PTR, o estado de conservação associado à presença de lesões bucais e o recebimento de orientação profissional. Sessenta usuários de PTR foram entrevistados e suas próteses avaliadas quanto à higiene, conservação e saúde bucal. Observou-se que 96,7% dos pesquisados não receberam orientação profissional, o método mecânico foi o mais utilizado para higienização e realizado três vezes ao dia (36,7%). A higiene das PTR apresentou-se moderada e as características funcionais estavam insatisfatórias. A queilite angular não teve significância estatística quando associada ao nível de higiene. A ausência de retenção e estabilidade estática associou com as lesões no maxilar inferior (p=0,02). As características deficientes das PTR representam uma tendência para a ocorrência de lesões bucais e os participantes, apesar da higiene frequente, não conheciam a forma correta de higienização e não receberam orientação que a PTR poderia causar lesões bucais.", "_i": "pt"}]

Are non-carious cervical lesions more frequent in sleep bruxism patients? / Lesões cervicais não cariosas são mais frequentes em pacientes com bruxismo do sono?

Objective: to verify the frequency in non-carious lesions in patients with and without sleep bruxism and to try to list the occurrence of such lesions in patients with this parafunctional habit. Material and Methods: 67 patients ranging from 18 to 70 years of age, which all signed a free and consent form were evaluated. Patients with neurological diseases and/or partially or totally edentulous were excluded from the study. Bruxism diagnosis was performed using a validated questionnaire based on the combination of at least two positive confirmations of bruxism. Diagnosis of non-carious cervical lesions (NCCL) was performed by a single calibrated examiner, using #5 clinical probe, intraoral mirror and air flow, analyzing all surfaces of the teeth present in the mouth. The lesions were classified as abfraction, abrasion or erosion. Statistical analysis was performed by U MannWhitney test, at 5% level of significance. Results: sixty patients were diagnosed with bruxism (91.3%) and only seven patients (8.7%) did not present this parafuctional habit. Regardless the gender, five patients (10.1%) presented absence of lesions and 62 patients (89.9%) presented some NCCL. 70% presented abfraction, 41% abrasion and no patient presented erosion. Statistical analysis showed a p-value of 0.03, which demonstrated significant statistical difference of NCCL between the groups. Conclusion: a higher frequency of NCCL in patients with bruxism was observed when compared to patients without this parafuction. (AU)

Objetivo: verificar a frequência de lesões não cariosas nos pacientes com e sem bruxismo do sono e tentar relacionar a ocorrência dessas lesões a esse hábito parafuncional. Material e Métodos: foram avaliados 67 pacientes com idade entre 18 e 70 anos, os quais assinaram um termo de consentimento livre e esclarecido. Foram excluídos da pesquisa pacientes com doenças neurológicas e/ou endêntulos parciais ou totais. O diagnóstico de bruxismo foi realizado através de um questionário validado que se baseiam na combinação de pelo menos duas constatações positivas de bruxismo. O diagnóstico das lesões cervicais não cariosas (LCNC) foi realizado por um único examinador calibrado, e observadas mediante utilização de sonda clínica n° 5, espelho clínico intraoral e jato de ar, analisando todas as faces de todos dos dentes presentes em boca. Essas foram classificadas em abfração, abrasão ou erosão. A análise estatística foi realizada pelo teste U de Mann-Whitney para tratamento estatístico com nível de significância de 5%. Resultados: sessenta pacientes foram diagnosticados com bruxismo (91,3%) e apenas sete pacientes (8,7%) não possuíam esse hábito parafuncional. Independente do gênero, cinco pacientes (10,1%) possuíam ausência e sessenta e dois pacientes (89,9%) possuíam presença de alguma LCNC. 70% possuíam abfração, 41% abrasão e nenhum paciente apresentou erosão. O teste estatístico obteve um p-valor igual a 0,03; demostrando uma diferença estatisticamente significativa da presença de LCNC entre os grupos. Conclusão: nota-se que houve uma maior frequência de LCNC em pacientes com bruxismo em comparação ao grupo que não apresentou essa parafunção. (AU)

Análise da influência da morfologia do modelo ósseo na distribuição das tensões do sistema de implante cone morse, método dos elementos finitos tridimensionais

O conhecimento do comportamento mecânico do sistema de implante corresponde a um importante parâ- metro no prognóstico de uma reabilitação protética. Objetivo: avaliar a influência do formato de tecido ósseo na distribuição de tensões no implante do tipo cone morse e tecido ósseo por meio do método dos elementos finitos tridimensionais. Materiais e método: foram utilizados três tipos de formatos de modelos para tecidos ósseos: a) paralelepípedo; b) tronco elíptico; c) gerado a partir dos dados de uma tomografia. Nos modelos tridimensionais, foram instalados implantes que receberam aplicação de duas cargas de 100 N no sentido craniocaudal: 1) na direção vertical ao longo do eixo axial e 2) na direção oblíqua a 45° do eixo axial de vestibular para lingual. Resultados: as tensões de von Mises máximas (MPa) nos modelos do implante cone morse (CM) e do tecido ósseo do tipo paralelepípedo foram de 14.30 no carregamento vertical e de 60.78 no carregamento oblíquo; no modelo de tecido ósseo elíptico, foram de 14.69 no carregamento vertical e de 71.66 no carregamento oblíquo; no modelo de tecido ósseo com a configuração originada da tomografia, foram de 15.04 no carregamento vertical e de 79.15 no carregamento oblíquo. Conclusão: o formato dos modelos de tecido ósseo influenciou no comportamento e na distribuição das tensões, sendo que o modelo gerado pelos dados da tomografia apresentou os maiores valores de tensões.

Electromyographic activity in patient with an inferior implant/tooth-supported overdenture: clinical report / Atividade eletromiográfica de um paciente com prótese inferior implantodentossuportada: Relato de caso clínico

Clinicians can find patients with one mandibular remaining tooth, and it is difficult to decide if the tooth has to be removed. When a clinician decides to maintain the tooth, it is common to question the masticatory load distribution divided between the tooth and implant. This paper reports a clinical case of patient with an implant/tooth-supported overdenture and elucidates the masticatory efficiency by electromyography activity analysis. The objective of this case report was to describe a clinical case of a patient with an implant/tooth-supported overdenture and to discuss the muscle response to this treatment. Electrical activities of the masseter and anterior temporal surfaces at maximum voluntary contraction were evaluated by electromyography during pre-treatment, immediately post-treatment,15 and 60 days after installation. When patienthas one remaining tooth in good condition, theimplant/tooth-supported overdenture can be recommended, to preserve the periodontal ligament and proprioception, and to minimize bone loss. Electromyography analysis showed that implant/tooth-supported overdenture is a viable treatment alternative, in muscular stand point, when the patient has a remaining tooth with good osseous support...

Os dentistas podem encontrar casos em que o paciente possui apenas um dente mandibular remanescente,sendo difícil decidir se o dente deverá ser extraído. Quando o clínico decide manter este dente, é comum surgirem dúvidas sobre como ocorre a distribuição da carga mastigatória em próteses suportadas por dente e implante. Este artigo relata a resposta muscular por meio de atividade eletromiográfica de um paciente reabilitado com uma prótese inferior implantodentossuportada. O objetivo deste artigo foi descrever este caso clínico e discutir a resposta musculatória neste tipo de tratamento. As atividades eletromiográficas dos músculos massetere temporal anterior superficial foram avaliadas durante o pré-tratamento, imediatamente após a instalação da prótese, 15 e 60 dias pós-tratamento.Foi verificado que quando o paciente tem um dente remanescente em condição de ser mantido, a prótese implantodentossuportada pode ser recomendada como tratamento, para preservação do ligamento periodontal e da propriocepção, e para minimizar a perda óssea. A análise eletromiográfica demonstrou que a prótese implantodentossuportada é uma alternativa viável de tratamento, do ponto de vista muscular, quando o paciente possui um dente remanescente com suporte ósseo adequado...

Effect of air-abrasion regimens and fine diamond bur grinding on flexural strength, Weibull modulus and phase transformation of zirconium dioxide.

PURPOSE: This study evaluated the effect of air abrasion and polishing regimens on the flexural strength of yttrium stabilized polycrystalline tetragonal zirconia (Y-TZP). METHODS: From Y-TZP blocks (InCeram 2000 YZ Cubes; Vita Zahnfabrik, Bad Säckingen, Germany) 120 bars (25 mm × 4 mm × 1.2 mm) were obtained according to ISO 6872:2008 and randomly divided into 4 groups: Group C: (control) without surface treatment (n = 30); Group APA: Air abrasion with aluminum oxide (44 µm) (n = 30); Group SC: Silica-coating (CoJet, 30 µm) (n = 30); Group FD: Fine diamond bur (n = 30). Subsequently, all specimens were subjected to 4-point bending test (in distilled water at 37 °C) in a universal testing machine (EMIC DL 1000; São José dos Pinhais, Paraná, Brazil); cross-head speed: 0.5 mm/min). The characteristic strength (σ0) of each specimen was obtained from the flexural strength test and evaluated using Weibull analysis. X-ray diffraction analysis was utilized to quantity the monoclinic phase. The surface topography of specimens was analyzed using 3D optical profilometer and scanning electron microscopy (SEM) after surface conditioning methods. The flexural strength data (σ4p) were statistically analyzed by 1-way ANOVA, Tukey test (α = 0.05) and Weibull (m = modulus, σ0 = characteristic strength) were calculated. RESULTS: The mean ± standard deviations (MPa) of the groups were as follows: C: 1196.2 ± 284.2a; APA: 1369.7 ± 272.3a; SC: 1207.1 ± 229.7a and FD: 874.4 ± 365.4b. The values (m) and (σ0) were as follows: C: 4.5 and 1308.12; APA: 5.9 and 1477.88; SC: 6.0 and 1300.28; and FD: 2.6 and 985.901, respectively. CONCLUSIONS: Air particle abrasion with neither silica nor alumina showed significant difference compared to the control group but grinding with fine diamond bur impaired the flexural strength of the zirconia tested.

Influence of CAD-CAM diamond bur deterioration on surface roughness and maximum failure load of Y-TZP-based restorations.

PURPOSE: To investigate the influence of CAD-CAM diamond bur deterioration on surface roughness (Ra) and maximum failure load (Lf) of Y-TZP-based ceramic (YZ) substructures (SB) veneered with a feldspathic porcelain. METHODS: Two sets of burs (B1 and B2) were used to fabricate 30 YZ SB each in a CAD/CAM system (Cerec InLab). The SB were identified (1-30) according to the milling sequence (MS). SEM images of the burs were recorded before milling, and after milling 15 and 30 SB. The SB Ra was measured. All SB were veneered, cemented onto a fiber reinforced epoxy resin die, and loaded to failure. Specimens from B1 group were cyclic fatigued (106 cycles) before loading to failure. Fractographic analysis was performed. Data were statistically analyzed using Student's t-test, Weibull analysis, Pearson's correlation and ANOVA (α= 0.05). RESULTS: The mean Ra value of B1 specimens was statistically greater than B2. Weibull modulus of B1 and B2 were statistically similar. The correlation between MS and Lf was not statistically significant for the groups. MS and Ra had significant correlation for both groups (B1: r= -0.514, P= 0.015; B2: r= -0.462, P= 0.03). Although the visual aspect (SEM) of the burs was similar after 30 millings, the mean Ra values were significantly different after 27 millings for B1 and 24 millings for B2.